100:2 Industrial Liquid Silicone Rubber Gypsum Wall Brick Crafts PU Resin Concrete Mold
Description of Tin Cure Silicone Rubber
HN-620 A/B is a two-component liquid silicone material. Two components are mixed in a ratio of 100:2. This product is cured at room temperature.
Application of Tin Cure Silicone Rubber
HN-620 A/B Industrial-grade liquid silicone rubber for manufacturing construction molds is suitable for the molding and reproduction of large-scale stones, gypsum, cement parts, cultural stones, artificial stones, Roman columns, stone carvings and other furniture, construction and decoration products; it can also be used for
resin handicrafts, gypsum handicrafts, soap handmade soaps, tire turning molds, and other segmented molds.
Technical parameter of Tin Cure Silicone Rubber
| Model | HN-620AB |
| Feature | high temperature resistance |
| Viscosity (cs) | 170000 |
| Gravity ( G/cm 3 ) | 1.06 |
| Hardness(A°) | 20 |
| Strength( MPa) | 3.1-3.6 |
| Tear Strength (kN/m ) | 19.8-24.3 |
| Elongation(%) | 600-720 |
| Linear Shrinkage(%) | ≤0.2 |
| Curing Agent Addition Ratio(%) | 2-3% |
| Operating Time( mins ) | 30-40 |
| Curing Time( hours ) | 3-4 |
Feature of Tin Cure Silicone Rubber
1. Strong tear resistance, high and low temperature resistance, acid and alkali resistance, and aging resistance;
2. Good fluidity, easy to release foam, easy to demould, and the finished product will not turn white;
3. The silicone mold can be turned over frequently and has a long service life;
4. The linear shrinkage rate is less than two thousandths;
5. Product color, hardness, viscosity, and operating time can be adjusted as needed.
Method of Application:
1 After shaking the curing agent (Part B), weigh the material according to the ratio of A: B = 100:2 and mix and stir evenly. The bottom and the walls of the container must be well scraped to ensure that the silicone and curing agent are fully mixed here. It must be stirred evenly. If not, it will affect the service life of the silicone mold.
2 Degas the well-mixed rubber under a vacuum, the vacuuming time should not be too long, generally not more than 10 minutes.
3 The mold can be fully cured after 4 hours at room temperature. Do not heat to cure.Even if you want to heat it up to accelerate its curing time, the temperature is not recommended to be higher than 100 °C. For best results, molds are best left for 24 hours before use.